Accelerated Corrosion of Fecralti Coating by in Situ Proton Irradiation in Molten Lead-Bismuth Eutectic

The synergistic effect of simultaneous proton irradiation and LBE corrosion on FeCrAlTi coating is investigated, and the surface morphology, elementary composition, microstructure and crystal structure of the formed oxide scale are systematically analyzed. The results reveal the accelerated LBE corrosion behavior of proton irradiated FeCrAlTi coating, which can be attributed to irradiation produced defects leading to enhanced diffusion, irradiation induced more porous oxide scale resulting in promoted short-circuit diffusion, and irradiation enhanced adsorption energy of O, Pb and Bi on coating surface contributing to intensive interface interaction.