Screening of the Biphenyl Polyamides Nanofilms Appropriate for Molecular Separation in Organic Solution Feed

Developing polymeric separation membranes that combine excellent solvent stability, high permeability, and customizable molecular weight interception remains a challenge. Herein, thin-film composite (TFC) polyamide (PA) membranes with poly(ether ether ketone) (PEEK) support and biphenyl-centered polyamides active layer were fabricated through interfacial polymerization technique for the first time. Enhanced solvent stability was exhibited by the fabricated membranes due to the intrinsic resistance to organic solvents possessed by PEEK and biphenyl polyamides. The separation performance of the obtained membranes was systematically studied by relating to the properties of PA nanofilms in terms of nano-mechanical strength, morphologies, and microporosity. The organic solvent nanofiltration (OSN) performance of the resultant membranes in terms of permeability and molecular weight cut-off (MWCO) could be regulated. The optimized membrane exhibited a pure solvent permeability as high as 21.6 L m- 2 h- 1 bar- 1 for acetonitrile and 14.0 L m- 2 h- 1 bar- 1 for methanol. It also showed excellent long-term durability with almost unchanged permeability as well as solute retention remained above 97.8 % after a cumulative OSN operation of N, N-Dimethylformamide (DMF) based feed for 240 h. In particular, OSN membrane with targeted MWCOs covering the range of 170-370 g center dot mol- 1 could be fabricated by selecting appropriate biphenyl acyl chlorides as building blocks. This approach offers a scalable and versatile platform for the development of solvent-stable, highly permeable, and customizable MWCO membranes for process-oriented OSN.